| Identification | Back Directory | [Name]
4-Aminobenzoic acid 4-aminophenyl ester | [CAS]
20610-77-9 | [Synonyms]
APAB
4-Aminophenyl 4-aminobenzoate
4-Aminophenyl4-Aminobenzoate>
4-AMinophenyl 4-aMinobenzoate(APAB)
Phenol, 4-aMino-, 1-(4-aMinobenzoate)
4-Aminobenzoic acid 4-aminophenyl ester
4-AMINOBENZOICACID4-AMINOPHENYLESTER/ETNT
Phenol, 4-amino-,4-aminobenzoate (ester) (9CI)
4-Aminobenzoic acid 4-aminophenyl ester (APAB) | [EINECS(EC#)]
810-934-8 | [Molecular Formula]
C13H12N2O2 | [MDL Number]
MFCD16038468 | [MOL File]
20610-77-9.mol | [Molecular Weight]
228.25 |
| Chemical Properties | Back Directory | [Melting point ]
179.0 to 183.0 °C | [Boiling point ]
465.6±30.0 °C(Predicted) | [density ]
1.286 | [storage temp. ]
Keep in dark place,Sealed in dry,Room Temperature | [form ]
powder to crystal | [pka]
4.01±0.10(Predicted) | [color ]
Light yellow to Brown | [InChI]
InChI=1S/C13H12N2O2/c14-10-3-1-9(2-4-10)13(16)17-12-7-5-11(15)6-8-12/h1-8H,14-15H2 | [InChIKey]
LOCTYHIHNCOYJZ-UHFFFAOYSA-N | [SMILES]
C1(OC(=O)C2=CC=C(N)C=C2)=CC=C(N)C=C1 |
| Hazard Information | Back Directory | [Chemical Properties]
off-white to white powder | [Uses]
4-Aminobenzoic acid 4-aminophenyl ester (APAB) acts as a polymer monomer to synthesise a series of polyesterimide (PEsI) copolymers with 4,4′-BPDA and TFMB. The average interchain distances of these polymers ranged from 4.6 to 5.7 ?, which increased with the increase of TFMB content.The glass transition temperatures (Tg) of PEsI-0.3 and PEsI-0.4 were 445°C and 455°C, respectively, whereas there was no significant change in the glass transition temperatures (Tg) of PEsI copolymers when APAB content was greater than 50 mol%. These PEsI copolymers have coefficients of thermal expansion (CTE): 3.8 ~ 24.2 ppm K-1, modulus: 5.7-7.8 GPa, tensile strength: 282-332 MPa, elongation at break: 10.2%-23.3%, and dielectric constants: 2.53-2.76. These PEsI copolymers can be used as novel base film materials for flexible printed circuit boards (FPCs). | [Materials Uses]
4-Aminobenzoic acid 4-aminophenyl ester can be used as a monomer to synthesize
transparent polyimide and polyimide composite materials for aerospace,
5G MPI and other applications. It can also be used as raw material for rubber antioxidant and optical brightener. |
|
|