| | Lithium trifluoromethanesulfonate Basic information |
| | Lithium trifluoromethanesulfonate Chemical Properties |
| Melting point | >300 °C (lit.) | | density | 1,9 g/cm3 | | storage temp. | Inert atmosphere,Room Temperature | | solubility | Water | | form | Powder | | color | White or colorless | | Water Solubility | soluble | | Sensitive | Moisture Sensitive | | BRN | 4301818 | | Stability: | hygroscopic | | InChI | InChI=1S/CHF3O3S.Li/c2-1(3,4)8(5,6)7;/h(H,5,6,7);/q;+1/p-1 | | InChIKey | MCVFFRWZNYZUIJ-UHFFFAOYSA-M | | SMILES | C(F)(F)(F)S([O-])(=O)=O.[Li+] | | LogP | 0.3 at 25℃ and pH1 | | CAS DataBase Reference | 33454-82-9(CAS DataBase Reference) | | EPA Substance Registry System | Methanesulfonic acid, trifluoro-, lithium salt (33454-82-9) |
| Hazard Codes | Xi | | Risk Statements | 36/37/38 | | Safety Statements | 26-36-37/39 | | WGK Germany | 3 | | F | 3-10 | | Hazard Note | Irritant | | TSCA | TSCA listed | | HS Code | 29049020 | | Storage Class | 11 - Combustible Solids | | Hazard Classifications | Eye Irrit. 2
Skin Irrit. 2
STOT SE 3 |
| | Lithium trifluoromethanesulfonate Usage And Synthesis |
| Chemical Properties | white powder | | Properties and Applications |
Lithium trifluoromethanesulfonate is highly soluble in water and organic solvents and shows excellent ion conductivity. It is highly soluble in polar organic solvents such as dimethyl carbonate (DMC), diethyl carbonate (DEC), ethyl acetate, and others. This compound exhibits good thermal stability and has a non-coordinating anion (triflate), which helps prevent unwanted reactions with other components in electrochemical systems.
| | Uses | Lithium trifluoromethanesulfonate is mixed with ceramic filler to prepare polyethylene oxide films in order to improve the electrochemical and mechanical characteristics of the membrane, which is used in the lithium batteries. It acts as a doping salt used in the preparation of nano manganese-composite polymer electrolytes. | | General Description | This product has been enhanced for energy efficiency. | | Synthesis |
A 316L stainless steel autoclave was charged with 1678 g of a 10.0% aqueous solution of lithium hydroxide and 424 g of calcium oxide, and the temperature was raised to 85 ° C, and the mixture was stirred for 3 hours. The reaction pressure was controlled by continuously feeding the trifluoromethane sulfonyl fluoride gas. The reaction time is 3.5 hours, then the reaction is kept for 3 hours, and then the temperature is lowered to 25 ℃. The reaction liquid is filtered to obtain the product lithium trifluoromethanesulfonate aqueous solution.
| | References | [1] Patent: CN105693561, 2016, A. Location in patent: Paragraph 0030 |