| | Epoxyacrylate Oligomer Basic information |
| Product Name: | Epoxyacrylate Oligomer | | Synonyms: | EBECRYL 600;EPOXYACRYLATE OLIGOMER, 2000-4000 MPA.S;EBECRYL 600?-5-10;EPOXY ACRYLATE OLIGOMER;EPOXY ACRYLATE | | CAS: | 71281-65-7 | | MF: | C27H32O8 | | MW: | 484.53818 | | EINECS: | | | Product Categories: | | | Mol File: | 71281-65-7.mol |  |
| | Epoxyacrylate Oligomer Chemical Properties |
| Fp | >109 °C | | InChI | InChI=1S/C27H32O8/c1-5-25(30)34-17-21(28)15-32-23-11-7-19(8-12-23)27(3,4)20-9-13-24(14-10-20)33-16-22(29)18-35-26(31)6-2/h5-14,21-22,28-29H,1-2,15-18H2,3-4H3 | | InChIKey | VZTQQYMRXDUHDO-UHFFFAOYSA-N | | SMILES | C(OCC(O)COC1=CC=C(C(C2=CC=C(OCC(O)COC(=O)C=C)C=C2)(C)C)C=C1)(=O)C=C |
| | Epoxyacrylate Oligomer Usage And Synthesis |
| Description | EBECRYL 600 (Epoxyacrylate Oligomer) is a photoactive prepolymer with low viscosity, little skin irritation and excellent pigment wettability. It is obtained from the esterification reaction of acrylic acid and epoxy soybean oil. The essence of the reaction is the addition reaction of carboxylic acid and epoxy group.
| | Synthesis | In a four-necked flask equipped with reflux condenser, stirrer, dropping funnel, thermometer, add a certain amount of epoxidized soybean oil, the oil bath heated to 85 when the proportional drop containing the catalyst triphenylphosphine, polymerization blocking agent hydroquinone and acrylic acid mixed solution, to control the rate of drop acceleration and increase the temperature of the oil bath while adding drops. After the mixed solution was added, the oil temperature was raised to 110C. At this time, the dropping funnel was removed and a thermometer was inserted to maintain a constant temperature of 110C in the bottle, until the acid value of the system was 5mgKOH/g, when the system was finished. |