| Company Name: |
Alfa Aesar |
| Tel: |
400-6106006 |
| Email: |
saleschina@alfa-asia.com |
| Company Name: |
Energy Chemical |
| Tel: |
400-0056266 |
| Email: |
sales8178@energy-chemical.com |
- TITANIUM MONOXIDE
-
- $10.00
-
2021-10-21
- CAS:12137-20-1
- Min. Order: 1KG
- Purity: 99%
- Supply Ability: 20 tons
- TITANIUM MONOXIDE
-
- $1.00
-
2020-01-15
- CAS:12137-20-1
- Min. Order: 1KG
- Purity: 99.0%
- Supply Ability: 100kg
Related articles - What is the crystal of TiO2?
- Titanium Dioxide Single Crystal is a single crystal from the Goodfellow range. Variations of these single crystals are availab....
- May 21，2024
|
| | Titanium monoxide Basic information |
| Product Name: | Titanium monoxide | | Synonyms: | Titanium oxide (TiO);Titanium oxide, alpha;titaniumoxide(tio);TITANIUM MONOOXIDE;TITANIUM(+2)OXIDE;TITANIUM(II) OXIDE;Titanium (II) oxide pellets, 8 to 9mm(0.32 to 0.36 in.) dia. x 6 to 7mm(0.24 to 0.28 in.) thick;TITANIUM (II) OXIDE, 99.9%, LUMPSTITANIUM (II) OXIDE, 99.9%, LUMPSTITANIUM (II) OXIDE, 99.9%, LUMPS | | CAS: | 12137-20-1 | | MF: | OTi | | MW: | 63.87 | | EINECS: | 235-236-5 | | Product Categories: | metal oxide;Inorganics | | Mol File: | 12137-20-1.mol |  |
| | Titanium monoxide Chemical Properties |
| Melting point | 1700°C | | Boiling point | >3000°C | | density | 4,95 g/cm3 | | Fp | >3000°C | | storage temp. | Store at room temperature, keep dry and cool | | form | pieces | | Specific Gravity | 4.95 | | color | yellow cubic crystals, crystalline | | Water Solubility | Soluble in concentrated sulfuric acid, concentrated hydrofluoric acid and alkali. Insoluble in water, diluted sulfuric acid, hydrochloric acid, nitric acid and organic solvents. | | Specific Heat Capacity | Cp(crystal): 0.63 J/(g·K), at 25℃ | | Crystal Structure | Cubic | | crystal system | Cube | | Space group | Fm3m | | Lattice constant | | a/nm | b/nm | c/nm | α/o | β/o | γ/o | V/nm3 | | 0.4182 | 0.4182 | 0.4182 | 90 | 90 | 90 | 0.0731 |
| | Dielectric constant | 110.0(Ambient) | | InChI | 1S/O.Ti | | InChIKey | OGIDPMRJRNCKJF-UHFFFAOYSA-N | | SMILES | O=[Ti] | | CAS DataBase Reference | 12137-20-1(CAS DataBase Reference) | | EPA Substance Registry System | Titanium oxide (TiO) (12137-20-1) |
| WGK Germany | 3 | | TSCA | TSCA listed | | Storage Class | 13 - Non Combustible Solids |
| | Titanium monoxide Usage And Synthesis |
| Chemical Properties | bronze pellets; fcc; weakly basic oxide with no important industrial uses [HAW93] [STR93] [KIR83] | | Chemical Properties | Titanium monoxide, TiO, has a rock-salt structure but can exist with both oxygen and titanium vacancies. For stoichiometric TiO, the lattice parameter is 417 pm, but varies from ca 418 pm at 46 atom % to 4162 pm at 54 atom % oxygen. Apparently, stoichiometric TiO has ca 15% of the Ti and O sites vacant. At high temperatures (>900 °C (1,652 °F)), these vacancies are randomly distributed; at low temperatures, they become ordered. Titanium monoxide may be made by heating a stoichiometric mixture of titanium metal and titanium dioxide powders at 1,600 °C (2,912 °F). | | Physical properties | Gold-bronze solid. Prepared
by mixing stoichiometric
amounts of Ti and TiO2 heated in a Mo-crucible at 1600°C
or by the reduction of TiO2with H under pressure at 130 atm and 2000°C. Slightly
paramagnetic solid with χm = +88 × 10–6 emu. | | Uses | Used for vacuum deposition. Also applications include sunscreens and UV-blocking in cosmetics, varnishes, wood preservatives, textile fibers, and packaging films. Also used as paint pigment, opacifying agent, welding rod fluxes, optical coatings, as a catalyst, ceramic finish coat, plastics, elastomers, coated fabrics, printing inks, roofing granules, glass, and in glazes. Also identified as Titanium monoxide. | | Definition | ChEBI: Titanium(II) oxide is a titanium oxide containing approximately equal numbers of titanium and oxygen ions. | | Preparation | Titanium monoxide or hongquiite (TiO) may be prepared by direct reduction by mixing stoichiometric amounts of titanium metal
and titanium dioxide into a molybdenum crucible at 1600°C or reduction of the titanium
dioxide with hydrogen under pressure at 130 atm and 2000°C.
Ti (s) + TiO2(s) —> 2 TiO(s) (1600°C)
| | Reactions | On heating the monoxide in air, the compound reverts to other titanium oxides as a function
of temperature increase:
TiO(s) —> Ti2O3(s) (200°C);
TiO(s) —> Ti3O5(s) (250–350°C);
TiO(s) —> TiO2(s) (350°C).
| | reaction suitability | reagent type: catalyst
core: titanium |
| | Titanium monoxide Preparation Products And Raw materials |
|